After-sales Service: | Online Technical Support |
---|---|
Highest Working Temperature: | 1500 |
Material: | Inorganic Siliceous & Calcareous |
Still deciding? Get samples of US$ 1/Piece
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment methods: |
![]() ![]() ![]() ![]() ![]() ![]() ![]() |
---|---|
Support payment in USD |
Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
MYREAL calcium silicate 220 is taking inorganic siliceous and calcareous as material and treated by special technology such as high temperature and high-pressure hydrothermal reaction, and the product has won ISO9001 certification. It has excellent performance under the temperature of 650ºC. The greatest advantage is it can provide nice protection to pipelines since it with super-low chloride ion content. Thanks to the improvement of producing technology, we have reduced the thermal conductivity from 0.065 to 0.049 at present.
Specification:
Description | MYREAL CALCIUM SILICATE INSULATION BOARD / PIPE | |
Maximum Use Temperature (ºC ) | 650 | |
Chemical Composition (%) | ||
SiO2 | 37-42 | |
CaO | 29-34 | |
Al2O3 | 10-12 | |
MgO | 1.8-2.1 | |
Color | White | |
Density (kg/m³) | 230±10% | 250±10% |
Modules of Rupture (MPa) | ≥0.30 | ≥0.45 |
Compressive Strength (MPa) | ≥0.50 | ≥0.60 |
Permanent Linear Shrinkage (%) | 650ºC x16h≤2.0 | |
Thermal Conductivity (W/m·K) | ||
100ºC | ≤0.057 | ≤0.062 |
200ºC | ≤0.069 | ≤0.074 |
400ºC | ≤0.098 | ≤0.109 |
Description | MYREAL CALCIUM SILICATE INSULATION BOARD | ||
Maximum Use Temperature (ºC ) | 1000 | ||
Chemical Composition (%) | (%) | ||
SiO2 | 46-48 | ||
CaO | 39-41 | ||
Al2O3 | 0.39-0.42 | ||
MgO | 0.5-0.7 | ||
Color | White | ||
Density (kg/m³) | 230±10% | 250±10% | 270±10% |
Modules of Rupture (MPa) | ≥0.45 | ≥0.50 | ≥0.55 |
Compressive Strength (MPa) | ≥0.75 | ≥0.85 | ≥0.95 |
Permanent Linear Shrinkage (%) | 1000ºC x16h≤2.0 | ||
Thermal Conductivity (W/m·K) | |||
100ºC | ≤0.065 | ≤0.067 | ≤0.072 |
200ºC | ≤0.075 | ≤0.077 | ≤0.082 |
400ºC | ≤0.091 | ≤0.096 | ≤0.103 |
600ºC | ≤0.132 | ≤0.136 | ≤0.138 |
It's commonly applied in insulation projects such as: tank and tank base, pipeline, vessel, equipment, cryogenic ship, etc. for petroleum, chemical, refrigeration, underground projects, shipbuilding, national defense and residential construction industries. It can be applied in severe environment like: low & cryogenics / hot temperature, underground, outdoors, flammable, wet, and chemical etc.